Abstract

In this study, the mechanical and flame-retardant properties of ethylene-propylene-diene-termonomer (EPDM) based rubber compounds and various other environmentally friendly inorganic flame retardants were investigated. Alumina trihydrate (ATH) and magnesium hydroxide (MDH) were used as inorganic flame retardants. The mechanical properties after thermal oxidation aging and the flame-retardant properties of the EPDM compounds were measured using a moving die rheometer, a universal testing machine, a compression set, and a UL 94 V flammability test. We focused on how the properties were affected by the type and amount of flame retardants. The results demonstrated that the optimal mechanical and flame-retardant V-0 grade properties were obtained at an ATH content of 200 phr.

Keywords: EPDM;mechanical properties;flame retardant;burn test